Sintered RdFeB magnets
Main features :
1) Chemical composition : Nd2Fe14B .Hard , brittle and easily corrosive.
2) Moderate temperature stability Neodymium magnets lose -0.09 ～- 0.13 % of Br /℃.The Max WorkingTemperature can be up to 200℃.
3) Excellent strength value.The highest (BH)max reaches up to 52 MGOe.
4) Extremely good resistance to demagnetization with Hcj The intrinsic coercive –Hcj is up to 30 KOe .
5) Demagnetization Curve with good rectangularity .Magnetic polarization strength is almost invariable in a wild range of demagnetizing filed. Shown in rectangular coordinates , the B-H demagnetization Curve is a straight line in the second quadrant and extending to the third quadrant.
6) Low eddy current loss.Higher resistivity than Sm-Co magnets , let alone ordinary metallic materials. In alternating magnetic field such as that in the Motor , magnets have lower eddy current loss,so devices work with less heat and lower temperature rise.
7) Effective surface treatment to prevent corrosion. To improve the anti-corrosion level , surface treatment is recommended. Some opitional coatings : Zn , Ni-Cu-Ni ,Epoxy , Silver , Gold , etc.
8) Favorable mechanical properties , relatively easy to machine. Customized ones are also available as per the protype drawings.
Don't place magnets near person wearing electrical medical equipment,such as pacemaker , because the magnetsmay result in malfunction of the equipment and endanger person’s life.Keep magnets away from magnetic memory media or other magnetic led sensitive devices such as magnetic cards ,tapes , poppy disks , hard disk drives , and watches , otherwise big block of magnets will strongly attract each other or attract iron steel pieces , which may cause serious injure to person . The magnets may break into pieces when collide each other or with other materials . Be Careful in assembling magnets and prevent the tiny fragments entering into eyes or causing other injuries .
Keep magnets in good condition and avoid following environment in case that the magnets may rust or become weak in mechanical or magnetic performance .
a) With acid , alkali,organic solvent or electrolytes
b) Immersed in water or in oil
c) Hydrogen atmosphere
d) Corrosive atmosphere such as Cl2, NH3,NOX,etc
e) With radioactive rays